The fabrication of a mullite-bonded cordierite body suitable for use as kiln furniture has been investigated in this article. First of all cordierite powder was synthesized by mixing talc, kaolin and alumina as starting materials, pressing and firing up to 1325oC. The amount of cordierite phase was estimated by an X-ray diffraction technique. The synthesized cordierite was then mixed with certain amounts of kaolin and alumina as the starting materials for mullite formation and the mixture was shaped by a pressing method, following by firing at different temperatures. The changes of density, porosity and cold crushing strength of the samples were measured as a function of heat treatment temperature. The results showed that these properties improve by a rise in temperature. The mullite formation within the samples was confirmed by an XRD method. The thermal expansion coefficient of the samples fired at 1350oC was determined by a dilatometer having an average value of 3.18×10−6 (1/K), which indicates an excellent thermal shock resistant for the samples. The microstructure of the fired samples was studied using scanning electron microscopy (SEM), which showed interesting results.
فایلهای پیوست :
An investigation on the properties and microstructure of mullite-bonded cordierite ceramics
  • دفتر مركزي: یزد، خیابان مطهری، پارک علم و فناوری، پردیس فناوری اطلاعات، واحد 101
  • آزمايشگاه: يزد، بلوار دانشجو، سه راه تعاون، مجتمع ادارات پارك علم و فناوري يزد- پرديس زيست فناوري و سيستمهاي پيشرفته - مجموعه آزمايشگاه سراميك
  • 035-37260108
  • 035-37260109
  • info@ictdc.com
نماد اعتماد الکترونیکی